Polymaker HT-PLA Teal Turquoise Filament 1.75mm 1Kg

Polymaker HT-PLA is a very easy-to-print high-temperature filament that provides reliable results for both beginners and professionals. It combines the easy handling of classic PLA materials with significantly increased heat resistance. Printed parts remain dimensionally stable up to 130°C, making the material suitable for applications that must withstand high thermal loads. The excellent layer adhesion ensures precise printing results, while warping is minimized. HT-PLA also impresses with a high printing speed of up to 300 mm/s. Through optional annealing (about 30 minutes at 80–100 °C), the mechanical properties and temperature resistance can be significantly improved. Of particular note is the good paintability, as known from classic PLA: surfaces evenly absorb paints and varnishes, making the filament ideal for model making, tabletop miniatures, cosplay props, or custom parts for vehicle interiors. Thus, HT-PLA opens up possibilities that would otherwise only be achievable with technical materials such as ABS or ASA – but without their disadvantages like limited color options, complex processing, or higher printing requirements. HT-PLA combines the strengths of technical materials with the user-friendliness of PLA. When processed, it shows low odor development, slightly more than regular PLA, which is almost odorless, but far more pleasant than ASA or ABS, which emit significantly stronger odors.

Properties:

HT-PLA is heat resistant and remains dimensionally stable up to 130°C.
The material offers easy printability combined with high performance.
Layer adhesion is reliable and ensures precise results.
Warping occurs only to a slight extent.
Low odor development, slightly more than PLA, but far more pleasant than ASA or ABS.
Optional annealing further improves properties.
Paintability as expected from PLA, ideal for model making, tabletop, and cosplay.
Offers the advantages of technical materials without their disadvantages in processing and color variety.

Recommended Print Settings:

Print temperature: 210–230 °C, recommended 230 °C
Heated bed: 25–60 °C, recommended 50 °C
Fan: 100%
Printing speed: up to 300 mm/s

Documentation:

Technical Data:

Manufacturer: Polymaker
Manufacturer SKU: PA17007
Color: Teal
Weight (net): 1 kg
Diameter: 1.75 mm
Tolerance: ±0.02 mm
Density: 1.287 g/cm³
Melt flow index: 22.6 g/10 min (210 °C/2.16 kg)
Tensile strength (XY): 42.86 MPa
Tensile strength (Z): 18.82–20.83 MPa
Elongation at break (XY): 1.9–2.8 %
Elongation at break (Z): 0.8–1.0 %
Flexural strength (XY): 66.75–74.04 MPa
Flexural strength (Z): 28.95–29.39 MPa
Flexural modulus (XY): 2893–3267 MPa
Flexural modulus (Z): 2411–2596 MPa
Impact strength (Charpy XY): 4.7–4.9 kJ/m²
Impact strength (Charpy Z): 4.4–4.5 kJ/m²
Heat deflection temperature (HDT 0.45 MPa): 156.2 °C (as printed), up to 155.2–156 °C (annealed)
Spool diameter outer: 200 mm
Spool width: 65 mm
Inner hole diameter: 55 mm
Weight (gross): 1291g
Dimension: 205 x 225 x 75mm